CONPATIBLE MODELS :

YAMAHA

MT-07 14-15

 

MATERIAL :

6061-T6 Aluminum Alloy: Silicon 0.4~0.8%, Copper 0.15~0.4%, Magnesium 0.8~1.2%, Chromium 0.404~0.35%, Ultimate Tensile Strength 290 MPa 42000 psi, Bearing Yield Strength 241 MPa 35000 psi, while thickness is less than0.25" (6.4mm)Tensile Strength is 8% or more. While thickness is greater than 0.25" (6.4mm), Tensile Strength is 10%.

 SURFACE PROCESSING:

Anodized color treatment: Corrosion resistant and 60 hours anti-UV endurance (testing under 100eV UV exposure for 60 hours before color start fading, whereas natural UV radiation is around 3~10eV).

 FEATURE:

The 6061 Aluminum has gone through T6 heat treatment and offers better strength, hardness and flexibility than average 6061. The crash pad is made from POM material and offers high tensile strength, effectively absorbing the impact and dispersing the force during an accident.